- Strong adhesive strength (24.5 MPa (250 kgf/cm2 ) or more)
- Long pot life and high workability
- The strength increases quickly and reaches approx. 90% of the maximum strength after 24 hours at room temperature (25 C).
- The main agent and curing agent can be mixed easily by measuring the equal quantities of the agents by eye.
-
ThreeBond 2083L
- Displays high bonding strength in the air, on wet surfaces and in water.
- Excellent low-temperature curability
- Putty resin excelling in workability on vertical surfaces
- Not containing phthalic ester
-
- High adhesion
- Excellent low-temperature curability
- Since the adhesive has low viscosity and is clear and colorless, the bonded parts are not so visible.
- The main agent and curing agent can be mixed easily by measuring the equal quantities of the agents by eye.
-
ThreeBond 2086N
- It excels in low-temperature curability and can cure at -5 C.
- t exerts adhesive force even on moist surfaces.
- High bonding strength
- After curing, it becomes a flexible body excelling in impact strength.
- The adhesive can be prepared by mixing equal parts of the main and curing agents measured by eye. Therefore, the mixing operation is easy
-
ThreeBond 2086T
- Excellent low-temperature curability.
- Low-viscosity and transparent adhesive allowing bonding areas to be unnoticeable
- With appropriate thixotropic property
-
ThreeBond 2088E
Cold-curing two-part epoxy resin with high adhesion under heat
- High adhesion
- Long pot life
- After the resin is cured at room temperature(25℃)for 7 days and at 120℃ for 1 hour, it shows adhesion of 50 kg/cm² or more and 100 kgf/cm² or more, respectively,at a measuring temperature of 200℃.
-
ThreeBond 2088J
- Long pot life at room temperature, low viscosity and excellent workability
- Cures to a solid excelling in heat resistance and vapor resistance by heating
- Displays high bonding strength
-
ThreeBond 2089B
- The base resin and curing agent are formed together. It is only necessary to cut and knead to cure the putty. No part of the putty will be wasted, and the working efficiency will be improved.
- Excelling in fast curability. It starts curing after 2 to 3 minutes and can be machined by tools, such as a cutter, after 1 hour. Excelling in curability at low temperatures
- It has excellent heat resistance.(Thermal decomposition starting temperature: 260°C)
- The putty epoxy resin does not sag even on vertical surfaces.
-
ThreeBond 2106G
- Excellent lap shear strength
- Well-balanced properties of cured agent
-
ThreeBond 2106H
- Formes a cured product with excellent tensile shear adhesive strength
- This is a curing agent with excellent transparency
- Well-balanced properties of cured agent